玻璃钢工艺管道参数
2017-02-20 来自: 潍坊科达玻璃钢有限公司 浏览次数:686
玻璃钢工艺管道参数表
DN(mm) | 0.6MPa | 1.0MPa | 1.6MPa | 2.5MPa | L(m) | A(m) | ||||
T(mm) | W(Kg/m) | T(mm) | W(Kg/m) | T(mm) | W(Kg/m) | T(mm) | W(Kg/m) | |||
15 | 4.5 | 0.50 | 4.5 | 0.50 | 4.5 | 0.50 | 4.5 | 0.50 | 1 | 0.8 |
20 | 4.5 | 0.60 | 4.5 | 0.65 | 4.5 | 1.65 | 4.5 | 0.65 | 1 | 0.8 |
25 | 4.5 | 0.80 | 4.5 | 0.80 | 4.5 | 0.80 | 4.5 | 0.80 | 1 | 0.8 |
32 | 4.5 | 1.10 | 4.5 | 1.10 | 4.5 | 1.10 | 4.5 | 1.10 | 1 | 0.8 |
40 | 4.5 | 1.30 | 4.5 | 1.30 | 4.5 | 1.30 | 4.5 | 1.30 | 3 | 2.0 |
50 | 4.5 | 1.70 | 4.5 | 1.70 | 4.5 | 1.70 | 4.5 | 1.70 | 3 | 2.0 |
65 | 4.5 | 2.20 | 4.5 | 2.20 | 4.5 | 2.20 | 5.5 | 2.40 | 6 | 2.0 |
80 | 4.5 | 2.40 | 4.5 | 2.40 | 4.5 | 2.40 | 5.5 | 2.80 | 6 | 3.0 |
100 | 4.5 | 2.75 | 4.5 | 2.75 | 5.5 | 3.50 | 5.5 | 3.50 | 6 | 3.0 |
125 | 5.0 | 3.80 | 5.0 | 3.80 | 5.5 | 4.20 | 6.5 | 4.90 | 6 | 3.0 |
150 | 5.0 | 4.50 | 5.5 | 5.00 | 6.0 | 5.60 | 7.5 | 6.90 | 12 | 3.0 |
200 | 6.0 | 7.50 | 6.4 | 8.10 | 7.5 | 9.70 | 9.5 | 11.7 | 12 | 3.0 |
250 | 6.0 | 9.20 | 6.6 | 10.3 | 8.7 | 13.8 | 11.5 | 17.8 | 12 | 4.0 |
300 | 6.5 | 12.1 | 7.4 | 13.7 | 10.0 | 19.0 | 13.5 | 25.3 | 12 | 4.0 |
350 | 7.0 | 14.3 | 8.0 | 17.2 | 10.8 | 23.5 | 16.0 | 34.6 | 12 | 4.0 |
400 | 7.3 | 17.4 | 8.4 | 20.1 | 12.7 | 31.4 | 18.0 | 44.1 | 12 | 4.0 |
450 | 8.5 | 23.0 | 9.6 | 26.1 | 14.0 | 39.2 | 20.0 | 55.5 | 12 | 4.0 |
500 | 8.8 | 26.3 | 10.2 | 31.0 | 14.0 | 43.4 | 22.0 | 68.1 | 12 | 6.0 |
600 | 9.0 | 32.3 | 12.2 | 44.2 | 15.5 | 57.4 | 26.0 | 97.2 | 12 | 6.0 |
700 | 10.0 | 42.4 | 13.5 | 57.5 | 18.7 | 81.3 | 12 | 6.0 | ||
800 | 10.7 | 51.4 | 15.2 | 74.3 | 12 | 6.0 | ||||
900 | 11.7 | 64.0 | 16.6 | 92.0 | 12 | 6.0 | ||||
1000 | 12.3 | 75.0 | 18.0 | 111 | 12 | 6.0 | ||||
1200 | 13.0 | 103 | 12 | 6.0 | ||||||
1400 | 17.2 | 149 | 12 | 6.0 | ||||||
1500 | 17.3 | 162 | 12 | 6.0 | ||||||
1600 | 18.0 | 12 | 6.0 | |||||||
1800 | 19.0 | 12 | 6.0 | |||||||
2000 | 23.0 | 12 | 6.0 | |||||||
2200 | 24.0 | &l | ||||||||